Comparative Assessment of Marginal Micro Leakage of Different Esthetic Restorative Materials Used on Primary Teeth: An In-vitro Study

Aim: The aim of the current investigation was to evaluate the marginal microleakage of various esthetic restorative materials applied to primary teeth. Materials and methods: A total of 75 noncarious primary molars that were removed for orthodontic intervention and teeth nearing exfoliation were chosen. One millimeter (mm) above the cementoenamel junction, on the buccal surface of the teeth, Class V cavities were prepared. William’s graded periodontal probe was used to standardize cavity preparation on all teeth. 3 mm was the cavity’s length, 2 mm in width, and 2 mm in depth. The teeth were then divided into three groups (25 samples in each group) according to the type of esthetic restorative material used. Group I: Resin-modified glass ionomer cement, Group II: Ormocer, Group III: Giomer. The samples underwent 500 cycles of thermocycling, with an immersion time of 60 seconds and a well time of 15 seconds, between 5 and 55°C. The samples were submerged in methylene blue dye for 24 hours at room temperature and dried. The samples were then divided into sections and examined with a stereomicroscope. Data was recorded and statistically analyzed. Results: The least marginal microleakage was found in the ormocer group (1.22 ± 0.01) followed by resin-modified glass ionomer cement group (1.31 ± 0.07) and the giomer group (1.78 ± 0.03). There was a highly statistically significant difference found between resin-modified glass ionomer cement group and the ormocer group, resin-modified glass ionomer cement group and giomer group. And no significant difference was found between the ormocer group and the giomer group. Conclusion: The present study concluded that there was some amount of microleakage in primary teeth in all restorative materials examined in this in-vitro investigation. However, the marginal sealing ability of ormocer was found highest compared to resin-modified glass ionomer cement and Giomer materials. Clinical significance: The primary reason dental restorations fail, particularly in Class V cavities, is microleakage since the margins of these restorations are typically found in the dentin or cementum. Assessing microleakage is a crucial step in determining the marginal integrity of restorative materials. Developing methods and resources that reduce the adverse effects caused by the restorative marginal seal failing would benefit from this.