Canal pretreatment using cold atmospheric argon plasma, chitosan and Chlorine p6 activated by photodynamic therapy with EDTA as a final irrigant on the pushout bond strength of fiber post

Aims: To evaluate the effect of contemporary root canal irrigants i.e., Cold atmospheric argon plasma (CAAP), Chlorine p6 (Clp6), and chitosan on the push-out bond strength (PBS) of glass fiber post (GFP) and marten hardness (MH) of root canal dentin compared to NaOCl+EDTA. Materials and methods: The anatomic crown of sixty human mandibular premolars was removed by transversal section till cement-enamel junction (CEJ). Root canals were prepared and canals were dried and obturated using gutta-percha points and AH plus sealer. Post space was prepared and specimens were arbitrarily divided into four groups based on the post-space irrigation. (n = 15) Group 1: 5.25% NaOCl + 17% EDTA, Group 2: CAAP + 17% EDTA, Group 3: Chitosan + 17% EDTA and Group 4: Clp6 + 17% EDTA. For MH evaluation five samples from each disinfected group were taken and MH was assessed with the help of an ultra microhardness tester. GFP was cemented using self-etch dual cure cement on the remaining 10 samples from each group. Samples were vertically planted in acrylic resin blocks 1 mm thick slices were subjected to push-out testing and failure mode analysis using a universal testing machine and Stereomicroscope. ANOVA and Tukey multiple comparison tests were used to compare the means of bond integrity attained (p = 0.05). Results: The maximum values of PBS and MH were displayed in group 1 (5.25% NaOCl + 17% EDTA) specimens. However, group 3 exhibited the minimum values of bond strength and MH scores. Intergroup comparison analysis revealed that group 2, group 3, and group 4 displayed comparable outcomes of PBS and MH (p > 0.05). The cervical and middle third of group 1 specimens displayed a cohesive type of failure. However, the apical section of group 1 and other tested groups exhibited the adhesive type of failure. Conclusion: Canal irrigation with 5.25% NaOCl and 17% EDTA appears to be better in terms of improving the bond integrity of fiber posts with no compromise in MH of the dentin as compared to the contemporary irrigant used.